4004 • 4008 • 4016 • 4026 • 4032 • 4052 • 4056 • 4085

Typical Physical Properties

Note: The following technical information and data should be considered representative

or typical only and should not be used for specification purposes.

3M™ Double Coated Urethane Foam Tape

Adhesive Type:*

Units

4004

100

4008

100

4016

100

4026

100

Adhesive Carrier:

Polyurethane Foam Polyurethane Foam Polyurethane Foam Polyurethane Foam

Thickness: Nominal

Thickness: Tolerance:

Color:

Release Liner:

Liner Color:

Approximate Density:

(Foam Only)

Standard Length:

Maximum Length:

Available Width:

Normal Slitting Tolerance:

Normal Tensile:

(“T” Block)

Jaw Speed 2 in/min

(50 mm/min)

Static Shear:

inch (mm)

inch

(mm)

inch (mm)

yard (meter)

yard (meter)

inch (mm)

inch (mm)

psi (kPa)

0.250 (6.4)

0.215-0.285

(5.46-7.24)

Natural

0.003 (0.08)

Green Plaid

12

(190)

18 (16.5)

25 (23)

46 (1168)

± 1/32 (± 0.8)

12 (85)

0.125 (3.2)

0.110-0.150

(2.79-3.81)

Natural

0.003 (0.08)

Green Plaid

15

(240)

36 (32.9)

50 (45.7)

46 (1168)

± 1/32 (± 0.8)

25 (170)

0.0625 (1.6)

0.045-0.080

(1.142-2.03)

Natural

0.003 (0.08)

Green Plaid

11

(175)

36 (32.9)

100 (91)

46 (1168)

± 1/32 (± 0.8)

50 (345)

0.0625 (1.6)

0.045-0.080

(1.142-2.03)

Natural

0.003 (0.08)

Green Plaid

18

(290)

36 (32.9)

100 (91)

46 (1168)

± 1/32 (± 0.8)

40 (275)

Measured at various

temperatures and

gram loadings.

72°F (22°C)

120°F (49°C)

gms

1000

500

1000

500

1500

1000

2000

1000

(1/2 sq. in. overlap).

150°F (66°C)

500

500

750

1000

Will hold listed

weight for 100 hours.

200°F (93°C)

250

250

750

750

Tensile Strength:

Elongation:

Temperature Resistance:

Short Term (Minutes, Hours)

Long Term (Days, Weeks)

psi (kPa)

%

°F (°C)

°F (°C)

90 (620)

90

380 (193)

220 (104)

160 (1100)

90

380 (193)

220 (104)

140 (965)

100

380 (193)

220 (104)

180 (1240)

100

380 (193)

220 (104)

Solvent Resistance:

UV Resistance:

Cold Flex at -20°F (-30°C):

No apparent degradation when exposed to splash

tests of most hydrocarbon solvents.

No apparent degradation when exposed to 7 days in U.V. chamber.

No cracking when flexed around a 1/4 in. (6.4 mm mandrel).

Thermal Conductivity:

Dielectric Strength:

(watt/metre Kelvin)

volts/mil

(volts/0.025 mm)

0.036

(0.062)

200-300

(200-300)

0.036

(0.062)

200-300

(200-300)

0.036

(0.062)

200-300

(200-300)

0.036

(0.062)

200-300

(200-300)

*3M™ Adhesive 100 is a firm acrylic pressure sensitive adhesive system. It features high ultimate bond strength, very good high temperature

and solvent resistance and very high shear holding power. Bond strength increases substantially with natural aging.